Forum etiquette

Our mission ...

This forum is part of our mission to promote the preservation of vintage computers through education and outreach. (In real life we also run events and have a museum.) We encourage you to join us, participate, share your knowledge, and enjoy.

This forum has been around in this format for over 15 years. These rules and guidelines help us maintain a healthy and active community, and we moderate the forum to keep things on track. Please familiarize yourself with these rules and guidelines.

Remain civil and respectful

There are several hundred people who actively participate here. People come from all different backgrounds and will have different ways of seeing things. You will not agree with everything you read here. Back-and-forth discussions are fine but do not cross the line into rude or disrespectful behavior.

Conduct yourself as you would at any other place where people come together in person to discuss their hobby. If you wouldn't say something to somebody in person, then you probably should not be writing it here.

This should be obvious but, just in case: profanity, threats, slurs against any group (sexual, racial, gender, etc.) will not be tolerated.

Stay close to the original topic being discussed
  • If you are starting a new thread choose a reasonable sub-forum to start your thread. (If you choose incorrectly don't worry, we can fix that.)
  • If you are responding to a thread, stay on topic - the original poster was trying to achieve something. You can always start a new thread instead of potentially "hijacking" an existing thread.

Contribute something meaningful

To put things in engineering terms, we value a high signal to noise ratio. Coming here should not be a waste of time.
  • This is not a chat room. If you are taking less than 30 seconds to make a post then you are probably doing something wrong. A post should be on topic, clear, and contribute something meaningful to the discussion. If people read your posts and feel that their time as been wasted, they will stop reading your posts. Worse yet, they will stop visiting and we'll lose their experience and contributions.
  • Do not bump threads.
  • Do not "necro-post" unless you are following up to a specific person on a specific thread. And even then, that person may have moved on. Just start a new thread for your related topic.
  • Use the Private Message system for posts that are targeted at a specific person.

"PM Sent!" messages (or, how to use the Private Message system)

This forum has a private message feature that we want people to use for messages that are not of general interest to other members.

In short, if you are going to reply to a thread and that reply is targeted to a specific individual and not of interest to anybody else (either now or in the future) then send a private message instead.

Here are some obvious examples of when you should not reply to a thread and use the PM system instead:
  • "PM Sent!": Do not tell the rest of us that you sent a PM ... the forum software will tell the other person that they have a PM waiting.
  • "How much is shipping to ....": This is a very specific and directed question that is not of interest to anybody else.

Why do we have this policy? Sending a "PM Sent!" type message basically wastes everybody else's time by making them having to scroll past a post in a thread that looks to be updated, when the update is not meaningful. And the person you are sending the PM to will be notified by the forum software that they have a message waiting for them. Look up at the top near the right edge where it says 'Notifications' ... if you have a PM waiting, it will tell you there.

Copyright and other legal issues

We are here to discuss vintage computing, so discussing software, books, and other intellectual property that is on-topic is fine. We don't want people using these forums to discuss or enable copyright violations or other things that are against the law; whether you agree with the law or not is irrelevant. Do not use our resources for something that is legally or morally questionable.

Our discussions here generally fall under "fair use." Telling people how to pirate a software title is an example of something that is not allowable here.

Reporting problematic posts

If you see spam, a wildly off-topic post, or something abusive or illegal please report the thread by clicking on the "Report Post" icon. (It looks like an exclamation point in a triangle and it is available under every post.) This send a notification to all of the moderators, so somebody will see it and deal with it.

If you are unsure you may consider sending a private message to a moderator instead.

New user moderation

New users are directly moderated so that we can weed spammers out early. This means that for your first 10 posts you will have some delay before they are seen. We understand this can be disruptive to the flow of conversation and we try to keep up with our new user moderation duties to avoid undue inconvenience. Please do not make duplicate posts, extra posts to bump your post count, or ask the moderators to expedite this process; 10 moderated posts will go by quickly.

New users also have a smaller personal message inbox limit and are rate limited when sending PMs to other users.

Other suggestions
  • Use Google, books, or other definitive sources. There is a lot of information out there.
  • Don't make people guess at what you are trying to say; we are not mind readers. Be clear and concise.
  • Spelling and grammar are not rated, but they do make a post easier to read.
See more
See less

Desoldering ICs

  • Filter
  • Time
  • Show
Clear All
new posts

    Desoldering ICs

    While the principles involved in desoldering an [wiki="Integrated Circuit"]IC[/wiki] are the same as those for any other part, the delicate nature of the component and the large number of pins can present a challenge.
    If the chip to be removed is to be used again, great care is required to ensure all joints are completely free of solder. Just one partially soldered pin is enough to hold a stubborn IC in place and locating which pin is still connected can be tricky. If a pin is not completely clear of solder, it is often easier to flow new solder into the joint and start again. Take care not to apply excessive heat which may damage the IC or fine traces on the circuit board. When done correctly, very little force will be required to remove the IC from the board; ideally, turning the board over and giving it a good tap should make the IC fall out. If you find yourself prying the chip out, check again for stuck pins. When possible, it pays to practice on junk boards and ICs before tackling important or rare ICs.
    If the chip to be replaced is defective, it is often easier to cut the body of the chip away from the pins before starting, then desolder the individual pins. This approach can also be gentler on the circuit board from which the chip is being removed. As each pin is removed individually, it?s easier to detect when the pin is free so excessive heat and pressure can be avoided. With all pins removed, the holes can then be cleared of solder using a desoldering pump or solder wick. Small traces of solder are not always worth removing and can, after heating, be poked through with a wooden toothpick. It is sometimes easier and/or safer to leave the old pins in place and simply solder the new chip to the old pins sticking out from the board.
    See Also

    • [wiki]Soldering ICs[/wiki]

    I am troubleshooting a card mounted 286 processor from a Telex 1280 at the moment. I wanted to be able to work on it on the bench and not inserted in the computers backplane. To make it easier to power the board and make the needed connections I desoldered a 16 bit card slot from an old junk motherboad a couple nights ago. It had been a while, but by the time I got that slot out I was desoldering like a pro

    I can personally attest to the adding a little solder back trick. If you have a pin that isn't quite clear or just didn't have a lot of solder to start with it really helps.


      Its all I have been doing lately. Socketed up a Issue 1 ZX81 and an Einstein VPU/VRAM for fault finding, the ZX81 has heavy corrosion and resoldering is the only way to get a flow. I do use plumbers flux as well on difficult highly oxidised boards.

      I am using a very old green RS components sucker and I thing its getting past its use by date.

      I am tempted by one of the desktop vacuum desoldering irons units similar to the ones at work. They make desoldering a breeze.

      However, I'm thinking I really need an extraction system to stop me breathing in all that lead etc.
      Current fleet
      TRS80 Model 4 - BBC B - Tatung Einstein - PCW9512 - PET 3032 - C64 - ZX81 - Spectrum 48K - Amiga A500 - Apple II europlus - Apple iMAC G3. Sharp MZ-80K. - IBM 5160 XT - Multibus 286/10 - Micro PDP 11/73 - Rainbow PC100A - MicroVax II - MicroVAX 3100, 3300, VAX 4000 VLC & 4000 Model 96 - AlphaStation 225 Apricot PC - Apple Performa 6200 - Apple Mac IIcx - Osborne 1 - ACT Sirius 1


        I think you're over-reacting on the lead stuff. You'd get more lead in your system by using Grecian Formula 16 to darken your graying hair.


          Originally posted by Chuck(G) View Post
          I think you're over-reacting on the lead stuff. You'd get more lead in your system by using Grecian Formula 16 to darken your graying hair.
          Hey !

          My hair is still naturally black, with no 'enhancement' thank you very much !

          Interesting about the fumes, I stopped actively doing soldering professionally around 96 and since then fume extraction (and everything else) has become so much more restrictive. After an hour of sniffing flux and solder fumes I did think it might be worth a small fan or some such.

          Do we think there is little hazard ?, not really looked into it myself.
          Current fleet
          TRS80 Model 4 - BBC B - Tatung Einstein - PCW9512 - PET 3032 - C64 - ZX81 - Spectrum 48K - Amiga A500 - Apple II europlus - Apple iMAC G3. Sharp MZ-80K. - IBM 5160 XT - Multibus 286/10 - Micro PDP 11/73 - Rainbow PC100A - MicroVax II - MicroVAX 3100, 3300, VAX 4000 VLC & 4000 Model 96 - AlphaStation 225 Apricot PC - Apple Performa 6200 - Apple Mac IIcx - Osborne 1 - ACT Sirius 1


            Lead, like mercury is most dangerous when it takes the form of organic compounds, which can be metabolized.

            Consider the dreaded mrecury, for example. You can hold the metallic element in your hands without significant danger to yourself. Calomel, (mercury chloride. Hg₂Cl₂) is an inorganic salt that was widely used as a purgative. Dimethyl mercury (CH₃)₂Hg) is an organic compound that's been documented as being able to slowly kill from a single droplet on the skin (cf. the tragic story of Karen Wetterhahn).

            Lead is much the same way--it's still used as flashing for roofs, in stained glass work, in storage batteries, fishing sinkers and a host of other things, including solder in metallic form). On the other hand, Lead Acetate ("sugar of lead" Pb(CH₃COO)₂) is somewhat toxic. It's used in Grecian Formula as a hair darkener, only because you're not likely to ingest it. Old flaking lead paint is dangerous, mostly to young children because it interferes with brain development if they eat it. But everything from battleships to bridges was painted with lead-based paint, so not so much for adults. My home town was home to American Lead Products. I think I'm still more-or-less functional. I've been soldering since age 10 and still use 50-50 solid-core solder in metalwork.


              I agree, the lead is a non-issue. The flux fumes are probably a greater threat, but I don't really worry about them either


                Old-style Sn-Pb solder uses a rosin flux. I've taken (string) bass rosin and dissolved it in alcohol and used it--works fine.

                You're probably in more danger of exposure if you burn pine in your fireplace.


                  exposure to chimney fires!


                    I will just keep sniffing then
                    Current fleet
                    TRS80 Model 4 - BBC B - Tatung Einstein - PCW9512 - PET 3032 - C64 - ZX81 - Spectrum 48K - Amiga A500 - Apple II europlus - Apple iMAC G3. Sharp MZ-80K. - IBM 5160 XT - Multibus 286/10 - Micro PDP 11/73 - Rainbow PC100A - MicroVax II - MicroVAX 3100, 3300, VAX 4000 VLC & 4000 Model 96 - AlphaStation 225 Apricot PC - Apple Performa 6200 - Apple Mac IIcx - Osborne 1 - ACT Sirius 1


                      I love the smell of soldering. It brings back recollections of happier times. I guess if it gives me cancer someday, that's alright.
                      -- Lee

                      If you get super-bored, try muh crappy Odysee channel: Old Computer Fun!

                      Looking For: Type 4 HDC for Tandy II/12/16/6000, Mac IIci hard drive sled, PC-era Tandy stuff, Weird Old Unix Stuff, Aesthetic Old Serial Terminals (HP and DG in particular)


                        How I desolder chips.
                        If I intend to toss the chip, I use a pair of flush dikes ( that means the cutting edge is not offset from the edge of one side of the cutters ). I cut the leads as close to the IC body as I can. I then use a small bench vice or similar holder to heat the solder from the bottom side of the board. I use sharp tweezers to grab the lead and quickly pull them out before the tweezers remove too much heat. If you miss reheat and try again. I use a full length pull-it to suck the solder out.

                        If I intend to remove the IC intact it is different. First, I heat the board from the bottom. Most leads are flared out in the hole. It is almost impossible to remove 100% of the solder with the lead up against the inside of the hole. While the solder is molten I bend the lead so it is half way across the width of the hole. ( the solder must be completely molten to the top of the board. ) I then use the pull-it to remove the solder. Heat from the top and remove the iron at the instant I energize the pull-it. I then use what I call the tink test. I use a small flat screw driver and stroke across the lead ( careful to not push so much it bends ) and listen to the sound. A dull tink means it still has solder. Refill the hole and repeat, never try to suck an almost empty hole.
                        No matter what, at the top of the board, the shoulders of the lead will be touching the board. Even with the best of suckers, there will be a little meniscus of solder between the two. I then use a pair of short needle nose pliers such the one blade is right at the board and the other is at the package and squeeze. If you've done good at removing the solder, it will easily pop from the board. Before doing this, always inspect to make sure you really did remove any visible solder.
                        If all went well the IC should now easily lift from the hole.
                        I didn't mention through this that always keep clean fresh solder in the joint and a clean fresh tinned iron. Never attempt to heat with an oxidized iron. You can remove old oxidized solder with the pull-it and replace with fresh flux and solder. Use the correct heat level for the joint you are desoldering. A 4 layer ground pin takes about a 700F heat while a feed through lead takes about 600F tip ( with 60-40 or better 63-37 solder ).
                        Never use plumber flux on a board. It is impossible to clean completely and will cause long term failures. Don't use water soluble unless you intend to completely submerse the board in water. Use a good rosin flux. Experiment on a clean fresh board. This is a test I often do with new unknown flux. I take a new clean board I solder two close leads but let the flux get between the leads. I then let it sit for a few days. I then measure the resistance between the leads. If it measures anything on my highest resistance, I don't use that flux. Remember, even if you can remove the flux from the bottom of the board it is almost impossible to remove it all from the top under the part without special cleaning equipment ( that is no longer legal in the US ).
                        With water soluble flux, I once used some that claimed I didn't need to remove the old flux after solder ( from a known brand ). This was on an analog board. Nothing worked right until I soaked and rinsed the board several times. For most digital, a small leakage is not an issue. For most analog, as seen recently it one of the board I helped fix on the MB, a tiny leakage makes a difference for a 555 reset circuit. Know your flux!
                        I've used solder wick in some cases. Use with care. it takes a hotter iron than you'd normally use on a regular lead. Make sure to bend it so it doesn't touch traces the don't have solder mask that you are not working on. I've seen too many ripped traces. It can be used well but it has its problems as well. With a large hot iron, it is good at removing solder from power plane joints. I have some in my tool box but prefer the pull-it type.
                        I generally don't like to use combined iron and sucking systems. You can't see how much you are bending the lead under the round end. They also are harder to keep clean unless you are moving fast. An oxidized tip is a real hazard. Many will turn up the temperature to compensate. When it does finally make thermal contact, it will often damage the bond between the board and the trace. Learn how much heat is needed for each joint use a tiny amount of fresh solder or a little flux to make first contact. On really old oxidized solder, always remove and replace with fresh.
                        Good luck
                        Last edited by Dwight Elvey; May 3, 2020, 08:31 AM.


                          Anyone use CHIPQUICK?


                            Kester 186 is your friend! You can get it through Amazon.



                              Originally posted by ibmapc View Post
                              Anyone use CHIPQUICK?
                              I've used it once. A friend gave me a small piece. It seems to work but I'm not all that sure what the potential of things like migration are. Metals are funny. It did seem to work. Once the solder was diluted, I could just warm it with a heat gun, much less than an iron's heat.
                              I've seen what high tin on copper does over time. It is not pretty. These low temperature alloys may not have any long term issues but I'd love to see what effect it has on boards that are 30 years old. One should clean it good and dilute with regular solder, in my thinking. I guess I'll never know, as I doubt I'll be able to wait that long.